Belzona 1311 Ceramic R-Metal 2kg Kit Metal Repair Composite Epoxy Resin Based Structural Adhesive Protection Against Erosion Corrosion Chemical Resistance Solvent Free Room Temperature Cure

Belzona 1311 Ceramic R-Metal 2kg one Set Kit Base A 1.666kg + Solidifier B 0.334kg = 2kg A 2-part epoxy-based repair composite designed for metal repair and protection against the effects of erosion and corrosion. This solvent-free repair composite has excellent chemical resistance and will bond to all metals and most other rigid surfaces. It is easy to mix and apply without the need for specialist tools and it cures at room temperature eliminating the need for hot work. It is ideally suited to be overcoated with Belzona 1321 Ceramic S-Metal to ensure long-lasting performance. Can also be used as a high strength structural adhesive for metal bonding and to create irregular load bearing shims. Long-term erosion and corrosion resistance Excellent bonding to almost any rigid surface including steel, aluminium, copper, brass, glass, wood and most plastics Excellent chemical resistance against a wide range of chemicals Reduced health and safety risks as it is solvent-free Application and cure at room temperature - no hot work involved No shrinkage, expansion or distortion Excellent electrical insulation characteristics Rebuilding and geometry reconstruction of centrifugal and positive displacement pumps damaged by erosion and corrosion Pit fill and resurface of heat exchangers, water boxes and tube sheets Repair of butterfly and gate valves, fans and kort nozzles deteriorated as a result of erosion, corrosion and cavitation Repair of pipe elbows damaged by impingement High strength structural adhesive for metal bonding Creation of irregular load bearing shims Working Life: At 77°F (25°C), the usable life of mixed material is 15 minutes. Colour: Grey Mixing Ratio by Weight (Base : Solidifier): 5:1 Mixing Ratio by Volume: 3:1 Mixed Density: 2.36 – 2.52 g/cm³

• Belzona 1311 Ceramic R-Metal. 2kg one Kit. Base A 1.666kg + Solidifier B 0.334kg = 2kg. Metal Repair Composite. Epoxy Resin Based. High strength structural adhesive for metal bonding. Protection against Erosion Corrosion. Chemical Resistance. Solvent Free. Room Temperature Cure
• Rebuilding and geometry reconstruction of centrifugal and positive displacement pumps. Pit fill and resurface. Creation of irregular load bearing shims. For heat exchangers, water boxes, tube sheets, butterfly repair, gate valves, fans, kort nozzles, pipe elbows. For Steel, aluminum, copper, brass, glass, wood and most plastics.
• Long-term erosion and corrosion resistance. Excellent chemical resistance. Application and cure at room temperature - no hot work involved. Reduced health and safety risks as it is solvent-free. Excellent electrical insulation. No shrinkage, expansion or distortion.
• Volume Capacity 25.3 in³ (415 cm³)/kg. 50.6 in³ (830 cm³)/2 kg unit. Color: Grey. Base Gel strength at 77°F (25°C): 150 – 350 g/cm. Solidifier Gel strength at 77°F (25°C): 40 – 150 g/cm. Mixing Ratio by Weight (Base : Solidifier): 5:1; by Volume: 3:1. Peak Exotherm Temperature: 210 – 230°F (99 – 110°C). Time to Peak Exotherm: 33 – 41 minutes. Slump Resistance: Nil at 0.5 inch (1.27 cm). Mixed Density: 2.36 – 2.52 g/cm³ VOC Content: 0.08% / 1.93 g/L
• Cure Times table 0.25 inch (6 mm) thickness. No loading or immersion: 4 hrs at 5°C, 3 hrs at 10°C, 2.5 hrs at 15°C, 1.75 hrs at 20°C, 1 hr at 25°C. Machining / light loading: 6 hrs at 5°C, 4 hrs at 10°C, 3 hrs at 15°C, 2 hrs at 20°C, 1.5 hrs at 25°C. Full mechanical / thermal loading: 4 days at 5°C, 2 days at 10°C, 1.5 days at 15°C, 1 day at 20°C, 20 hrs at 25°C. Immersion in chemicals: 5 days at 5°C, 4 days at 10°C, 3 days at 15°C, 2 days at 20°C, 1.5 days at 25°C.